Matting agents(Indoor)
| Product name | Application | Processing & Use level | Characteristics |
| K7567 | Functional leveling agent | □ Extrude after premixing<br> □ Dosage is 0.7-1.5% of total formula weight | ■ Prevent pits, pinholes, fish eyes, etc.<br> ■ Excellent leveling performance and weather resistance, good compatibility |
| K7572 | Functional leveling agent | □ Extrude after premixing<br> □ Dosage is 0.6-1.5% of total formula weigh | ■ Significantly improve the melt flow of the system<br> ■ Prevent pits, pinholes, fish eyes, etc.<br> ■ The coating film has excellent leveling and fullness |
| SA88 | Leveling agent | 0.8-1.2% of the formula | Applicable to various powder paint, the overall situation is good, easy to control Promoting flow flat, significant effect . Enhance the powder loosening, enhancing the rate of powder |
| K7573 | Leveling agent | 0.6-1.5% of the formula | Preventing defects such as pits, pinholes, and fisheyes; Excellent leveling performance and weather resistance; Good film appearance and recoatability. |
| Product name | Application | Processing & Use level | Characteristics |
| SA550 | Matting agent (GMA resin) | □ Incorporated into formula before extrusion<br> □ Epoxy value is about 700 | ■ The lowest gloss＜5%(60°)<br> ■ Excellent weather resistance and anti-yellowing |
| SA580 | GMA matting resin | □ Premix with binder before extrusion<br> □ Epoxy value approx 650 | ■ Gloss range 1-10%<br> ■ Fine and smooth levelling<br> ■ Excellent impact and bending resistance |
| SA300 | GMA resin | □ Incorporated into formula before extrusion<br> □ Epoxy equivalent value is about 300 | ■ Increase the cross link density <br> ■ Improve the mechanical strength and heat resistance,chemical resistance |
| Product name | Application | Processing & Use level | Characteristics |
| K7318 | Low temperature curing accelerator | □ Incorporated into formula before extrusion<br> □ 0.5-2% by weight of total formula | ■ Reduce curing temperature,shorten curing time<br> ■ Improve leveling and anti-yellowing<br> ■ Reduce the gloss fluctuations with curring temperature |
| SA316 | Curing accelerator | □ Incorporated into formula before extrusion<br> □0.05-0.5% by weight of total formula | ■ 100% active constituent<br> ■ Reduce curing temperature,shorten curing time |
| K7312 | Low temperature curing accelerator | □0.5-1% by weight of total formula | Significantly improve the solvent resistance and impact resistance of the coating film. Improve the gloss stability of polyester/GMA matting system. Does not affect leveling and clarity of the coating film. |
| Product name | Application | Processing & Use level | Characteristics |
| SA2165 | Matting agent for hybrid |
□ Incorporated into formula before extrusion
□1-5% by weight of total formula |
■ Provide 12-70%(60°) of gloss
■ Wide range of applicability to polyester resins ■ Good flow and anti-yellowing |
| SA2165D | Matting agent for hybrid |
□ Incorporated into formula before extrusion
□ 1-5% by weight of total formula |
■ Provide 8-60%(60°) of gloss
■ Good storage stability ■ Lower gloss with lower usage |
| K7227 | Matting agent for hybrid |
□ Incorporated into formula before extrusion
□ 1-4.5% by weight of total formula |
■ Provide 3-40%(60°)of gloss
■ Cost saveing ■ Improve mechanical property |
| K7232 | Matting agent for hybrid |
□ Incorporated into formula before extrusion
□ 1-5% by weight of total formula □ 1phw K7232 react with 2.5phw epoxy |
■ lowest gloss approx 3%
■ Good levelling ,storage stability improvement ■ Improving applicability to polyester resins |
| K7225 | Matting agent for hybrid |
□ Incorporated into formula before extrusion
□ 1-4.5% by weight of total formula |
■ Provide 6-60%(60°) of gloss
■ Excellent flow and anti-yellowing ■ Wide range of applicability to polyester resins Jietonda® K7225 |
| SA2065K | Physical Matting Agent for Hybrid System | □ Extruded after premixing, the dosage is 1-4.5% of total formula weight |
■ Provides 5-70% (60 °) gloss
■ Good leveling and storage stability ■ Low resin selectivity for wide range baking |
| K7237A | Physical Matting Agent for Hybrid System | □ Extruded after pre-mixing, the amount is 1-5% of the total weight of the formula. One part of K7233 requires 1.5 parts of E-12 epoxy | ■ Provides a minimum of about 2% (60 °) gloss<br> ■ Excellent storage performance<br> ■ Good leveling and strong resin adaptability |
| K7232D | matting hardener for hybrid | Incorporated into formula before extrusion 1-5% by weight of total formula 1phw K7232D react with 1.5phw epoxy | Excellent matting effect, the lowest gloss can reach 5% (60°) Excellent leveling performance and surface fineness; Excellent storage stability ; Environmental protection and low smoke. |
| Product name | Application | Processing & Use level | Characteristics |
| SA206A | Matting agent for PES/TGIC | □ Incorporated into formula before extrusion<br> □ 1-3% by weight of total formula | ■ Provide 30-70%(60°) of gloss<br> ■ Good weather resistance and low usage |
| K7216 | Matting agent for PES/TGIC |
□ Incorporated into formula before extrusion
□ 2-6% by weight of total formula |
■ Provide 10% (60°)of gloss
■ Good flow and excellent anti-yellowing ■ Low wax |
| SA2061B | Matting agent for PES/TGIC | □ Dry blend<br> □ 1-1.5% by weight of total formula | ■ Provide 10-40% (60°)of gloss<br> ■ Low usage and good gloss stability |
| SA2068 | Matting hardener for PES/TGIC |
□ Incorporated into formula before extrusion
□ 1-5% by weight of total formula |
■ Provide 10%(60°) of gloss
■ Good flow and good film hardness |
| K7217A | Matting agent for PES/TGIC | □ Incorporated into formula before extrusion<br> □ 1-5% by weight of total formula | ■ Provide 16%(60°) of gloss<br> ■ Excellent gloss stability and and anti-yellowing |
| K7212 | PES / TGIC system physical matting agent | □ Extruded after pre-mixing, the dosage is 2-6% of total formula weight |
■ Provides about 20-60% (60 °) gloss
■ Good gloss stability ■ Good leveling and anti-yellowing |
| K7215 | Matting agent for PES/TGIC | Extruded after pre-mixing, the dosage is 4-6% of total formula weight | Provide lowest 5% (60°) gloss Excellent leveling with good mechanical property . Good stability for baking, recommended to use in anti-yellowing condition. |
| Product name | Application | Processing & Use level | Characteristics |
| K7656 | Degassing agent for powder coatings |
□ Premix with binder before extrusion
□ 0.5-2% by weight of total formulation |
■ Reducing surface defects such as pits and pinholes
■ Without affecting coating gloss and screen printing ■ Non-yellowing,suitable for HAA system |
| SA500 | Slip and Degassing agent |
□ Incorporated into formula before extrusion
□ 0.5-1% by weight of total formula |
■ Improve the film appearance and anti-yellowing
■ Substitute of benzoin |
| SA501 | Film hardening agent |
□ Incorporated into formula before extrusion
□ 0.5-1% by weight of total formula |
■ Improve the hardness and smoothness of film |
| SA5060 | Anti foaming agent |
□ Incorporated into formula before extrusion □ or dry blend
□ 0.5-1.5% by weight of total formula |
■ Eliminate pinholes,bubbles and craters
■ Used on porous substrates,such as cast iron ■ cast aluminum alloys |
| SA5066 | Special film hardening agent |
□ Incorporated into formula before extrusion □ or dry blend
□ 0.5-1.5% by weight of total formula |
■ Increasing hardness, scratch/friction resistance |
| K7661 | Degassing agent for powder coatings |
□ Premix with binder before extrusion or dry belend
□ 0.5-1.5% by weight of total formulation |
■ High degassing efficiency
■ Recommended for porous substrates |
| Product name | Application | Processing & Use level | Characteristics |
| K7101 | Epoxy hardener/curing accelerator |
□ Incorporated into formula before extrusion
□ As curing agent,e the use level is 2-4phr on epoxy resin |
■ Excellent flow and low usage
■ Used as curing agent, curing @120℃/30min ■ Used as accelerator, curing @240℃/30s |
| K7104 | Epoxy hardener |
□ Incorporated into formula before extrusion
□ As sole curative the use level is 3-5phr on epoxy resin |
■ Curing @ 140℃/15min or 240℃/30s
■ Applied for thick film coatings or FBE coatings ■ Good mechanical properties ■ Good chemical resistance |
| K7108 | Epoxy hardener |
□ Incorporated into formula before extrusion
□ As sole curative the use level is 4-6phr on epoxy resin |
■ Curing @ 150℃/10min or 240℃/2min
■ Applied for thin film decorative coatings or functional epoxy powder coatings ■ Good film appearance and mechanical strength |
| SA31 | Epoxy hardener/curing accelerator |
□ Incorporated into formula before extrusion
□ As accelerator, use level is 0.1-0.5% on total formula |
■ For functional or decorative powder coatings
■ Curing @ 140℃/30min |
| SA2830 | Epoxy hardener |
□ Incorporated into formula before extrusion
□ 3.5-4.5phr on epoxy resin |
■ For functional or decorative powder coatings
■ Curing @ 180℃/15min |
| SA2831 | Epoxy hardener (accelerated DICY) |
□ Incorporated into formula before extrusion
□ 4-5phr on epoxy resin |
■ For functional or decorative powder coatings
■ Curing @ 160℃/12min or 200℃/5min |
| SA3120 | β-HAA hardener |
□ Incorporated into formula before extrusion
□ Hydroxyl equivalent value is about 84 |
■ Eco-friendly,Low-toxicity,anti-yellowing
■ Exterior application, Substitute of TGIC |
| K7150 | Blocked polyisocyanate curing agent for PU powder coatings | It is recommended to cure with hydroxyl polymer in equivalent amount (13:87 for polyester with hydroxyl value of 30; 20:80 for polyester with hydroxyl value of 50) | Extremely high crosslink density , excellent surface hardness and chemical resistance for coating . Excellent leveling and smoothness. Excellent weather resistance. |
| K7152 | Blocked polyisocyanate curing agent for powder coatings | It is recommended to cure with hydroxyl polymer in equivalent amount 13:87 for polyester with hydroxyl value of 30; 20:80 for polyester with hydroxyl value of 50 | Extremely high crosslink density , excellent surface hardness and chemical resistance for coating . Excellent leveling and smoothness. Excellent weather resistance and anti yellowing performance. |
| Product name | Application | Processing & Use level | Characteristics |
| SA207 | Texture additive |
□ Incorporated into formula before extrusion
□ 0.08-0.15% by weight of total formula |
■ low usage
■ Impart sand grain finishes ■ Use for electrical appliances and IT equipments |
| SA2072 | texture additive |
□ Incorporated into formula before extrusion
□ 0.1-0.2% by weight of total formula |
■ low cost
■ Impart sand grain finishes ■ For almost all kinds of powder coatings |
| SA208 | Special texture additive |
□ Incorporated into formula before extrusion
□ 3.5-5% by weight of resin |
■ For almost all kinds of powder coatings
■ Impart special texture finishes such as wrinkle, reticulated, vein, embossed and grained |
| K7726 | texture additive | □ Incorporated into formula before extrusion □ 0.2-0.6% by weight of total formula | ● It can form a sand-like coating with excellent wear resistance. ● The sand texture surface is smoother and more delicate. ● Suitable for powder coatings of any system, such as pure epoxy, epoxy/polyester, polyester/TGIC or HAA and PU. |
| Product name | Application | Processing & Use level | Characteristics |
| SA2483 | Charge enhancing agent |
□ Incorporated into formula before extrusion
□ 0.3-0.6% by weight of total formula |
■ Enhance the conductivity
■ Improve the film appearance ■ Anti yellowing |
| SA2485 | Charge enhancing agent |
□ Incorporated into formula before extrusion
□ 0.2-0.5% by weight of total formula |
■ Excellent conductivity performance
■ Improve the film appearance and flow ■ Better overall performance than SA2483 |
| SA2486 | Charge enhancing agent |
□ Incorporated into formula before extrusion
□ 0.2-0.4% by weight of total formula |
■ Excellent conductivity performance
■ Use for both corona gun and tribo gun |
| SA2487 | Charge enhancing agent | □ Incorporated into formula before extrusion □ 0.3-1.5% by weight of total formula | ■ No catalytic activity, does not affect the gloss of the coating and the gel time of the coating. ■ Good geothermal stability and anti-yellowing properties. ■ Does not affect powder storage stability. |
| K7017 | Charge enhancing agent | □ Incorporated into formula before extrusion □ 0.3-1.5% by weight of total formula | ■ No catalytic activity ,so no negative effect to the gloss of coating and gel time . ■ Good thermal stability and anti-yellowing properties. |
| Product name | Application | Processing & Use level | Characteristics |
| SA516 | Pigment dispersant |
□ Incorporated into formula before extrusion
□ 0.5-1% by weight of total formula |
■ Good pigment dispersing ability
■ Provide better color strength |
| K7005 | Anti-yellowing agent | □ Extruded after premixing, the dosage is 0.3-1% of the total weight of the formula |
■ For a variety of powder coating systems, especially HAA systems
■ Can significantly inhibit the yellowing of powder coatings caused by gas baking or electric baking |
| K7301A | Bonding additive | Refer to the TDS |
■ Improve the metal effect of coatings
■ Increase bonding temperature and anti caking ■ Reduce the dosage of metal pigments |
| SA5501 | Stabilizer for metal pigment |
□ Dry blend
□ 2-3% by weight of total formula |
■ Inhibiting from blackening, spot-formation and loss of brilliance of metallic coatings
■ Improve heat resistance |
| SA5502 | Dry powder flow additive |
□ Dry blend
□ 0.1-0.5% by weight of total formula |
■ Improving fluidity of coating powders
■ Anti caking ■ Enhancing electrostatic spray efficiency ■ Controlling film thickness for thin coating |
| K7921 | Adhesive modifier | Extruded after premixing, the dosage is 0.8-1.5% of the total weight of the formula | Improve the adhesion of the coating to metal substrates such as stainless steel and galvanized sheet, improve the flexibility of the coating without affecting the weatherability |
| K7010A | Special anti-caking additive | □ Dry blend □ 0.2-0.4% by weight of total formula | ■ Anti caking ■ For almost all kinds of powder coatings ■ Improving fluidity of coating powders |
| K7658 | surface wetting modifier | □ Incorporated into formula before extrusion □ 0.5-2% by weight of total formula | Good pigment and filler wetting and dispersing properties and allow to increase the amount of pigment and filler. Good wetting performance, improve the coating fog, improve the clarity and freshness of the coating. |
| K7771 | wear-resistant agent | □ Incorporated into formula before extrusion □ 0.2-0.5% by weight of total formula | Can form a coating with excellent wear resistance. Especially suitable for sand texture formula. |
| K7004 | Anti-yellowing agent | □ Extruded after premixing, the dosage is 0.5-1.5% of the total weight of the formula | Significantly improving discoloration and performance deterioration because of gas baking ; Can be used in PES/TGIC and PES/H AA systems, etc. |
| K7007 | Anti-yellowing agent | □ Extruded after premixing, the dosage is 0.2-1% of the total weight of the formula | Can significantly inhibit yellowing of powder coating caused by electric baking and gas baking. Can significantly inhibit the aging of the powder coating caused by high temperature baking, can withstand high temperature baking at 220-250 ℃. |
| K7010B | Anti caking agent | □ Dry blend □ 0.1-0.4% by weight of total formula | Significantly improve the dry powder fluidity and construction No harm to the leveling and mechanical properties of the coating. |
| K7923 | Adhesion promoter | Extruded after premixing, the dosage is 0.5-1.5% of the total weight of the formula | Significantly improve the adhesion of the coating to special metal substrates such as galvanized, magnesium aluminum alloy; |
PRODUCTS
HOTLINE:
+86-564-3711165
+86-
Mobile version
Search
| Add: 15 Li Dun, North Outskirts of Luan City, Anhui, P, R, China P.C.:237158 | |
| Tel: +86-564-3711165 , +86-564-3711777 | |
| Fax: +86-564-3711167 | E-mail: [email protected] |
Copyright(C)2019, Lu'An Jietonda New Material Co.,Ltd. All Rights Reserved. Supported by ChinaChemNet ChemNet Toocle Copyright Notice 京ICP證000000号
·